Aligned fiber reinforced molding

ABSTRACT

Methods and apparatus for additive manufactures of complex parts using co-aligned continuous fibers are disclosed. Filament subunits having complex shapes are fabricated and inserted into a mold cavity. The layup is compression molded to form a complex part having high tensile strength.

FIELD

Methods of fabricating high strength complex parts are disclosed. Shapedsubunits of fiber-reinforced filament are set in a molding cavity andcompression molded to provide high strength complex parts. High strengthparts can also be fabricated by drawing filer-reinforced filament andjoining filament sections.

BACKGROUND

Automated fiber placement or filament winding is a known method offorming aligned fiber-containing parts using impregnated tapes ofthermoplastic or thermosets. The process involves winding unidirectionaltape onto a mandrel by means of a rotating drive. Fiber placement iscontrolled by a carriage that moves parallel to the axis of the rotatingmandrel and controls fiber deposition with a pay-out eye. This processrelies on tape tension as the tape is wrapped onto a mandrel toconsolidate fibers and eliminate slack, voids and wrinkles. As a resultof the deposition method, filament winding is suitable for making alimited selection of shapes, in particular tubular- and tank-shapedparts with convex surfaces.

Automated tape laying and three-dimensional printing/additivemanufacturing are other known methods of forming alignedfiber-containing parts with impregnated tapes of thermoplastic orthermosets. These processes use automated robots or electromechanicalmotion systems to lay one or several layers of fiber tape or tows onto amold or onto a build surface to produce a part or structure. Limitationsexist for these layer-upon-layer deposition methods.

Compression molding is a known method of forming randomly aligned fiberparts with short sections of thermoplastic impregnated tape.

Resin transfer molding (RTM) is a known method of transferring a liquidpolymer matrix into a complex mold where the polymer permeates in situfiber reinforcement then hardens.

Methods of fabricating high strength complex thermoplastic parts aredesired.

SUMMARY

According to the present invention, fiber-reinforced composite partscomprise one or more sections, wherein, at least one of the one or moresections comprises two or more aligned fiber portions; and each of thetwo or more aligned fiber portions independently comprises a pluralityof co-aligned continuous fibers within a composition.

According to the present invention, method of fabricating afiber-reinforced composite part comprise; providing one or more filamentsubunits, wherein, each of the one or more filament subunitsindependently comprises a linear filament subunit, a shaped filamentsubunit, or a combination thereof; and at least one of the one or morefilament subunits comprises a first composition and a plurality ofco-aligned continuous fibers; placing the one or more filament subunitsinto a mold cavity to form a layup; and compression molding the layup toprovide a fiber-reinforced composite part.

According to the present invention, fiber-reinforced composite parts arefabricated according to the methods according to the present invention.

According to the present invention, methods of fabricating one or moreshaped filament subunits, comprise: securing a section of each of one ormore filaments; and shaping the one or more filament sections to provideone or more shaped filament subunits.

According to the present invention, shaped filament subunits arefabricated according to method of the present invention.

According to the present invention, filament subunit fabricationapparatus, comprise: a filament feeder configured to advance filament;securing device configured to secure and to manipulate a section of theadvancing filament; a heating element configured to heat a portion ofthe secured filament section; and a shaping element configured to shapeand to cool the heated portion of the filament section.

According to the present invention, methods of fabricating a part,comprise securing one or more filaments to a first anchor; and extendingthe one or more filaments in a direction away from the first anchor toprovide the part.

BRIEF DESCRIPTION OF THE DRAWINGS

The drawings described herein are for illustration purposes only. Thedrawings are not intended to limit the scope of the present disclosure.

FIGS. 1A-1F show linear and shaped filaments subunits and the assemblyof the filament subunits to form a layup for fabricating a partaccording to the present disclosure.

FIG. 2A shows the layup of FIG. 1F in a molding cavity.

FIG. 2B shows a part fabricated by compression molding the layup shownin FIG. 6A. FIG. 3A shows three shaped filament subunits according tothe present disclosure.

FIGS. 3B-3D shows steps in the assembly of the shaped filament subunitsshown in FIG. 3A according to the present disclosure.

FIG. 3E shows a finished part fabricated by compression molding thelayup of shaped filament subunits shown in FIG. 3D.

FIGS. 4A-4B show views of a bend in a shaped filament subunit accordingto the present disclosure.

FIGS. 5A-5C show cross-sectional views of shaped filaments according tothe present disclosure.

FIG. 6 shows an example of a filament subunit fabrication apparatusaccording to the present disclosure.

FIG. 7 shows an example of a filament shaping apparatus according to thepresent disclosure.

FIGS. 8A-8F show examples of layups with multiple filament subunits.

FIG. 9 shows the stress profile of a part fabricated using methodsaccording to the present disclosure.

Reference is now made in detail to embodiments of the presentdisclosure. While certain embodiments of the present disclosure aredescribed, it will be understood that it is not intended to limit theembodiments of the present disclosure to the disclosed embodiments. Tothe contrary, reference to embodiments of the present disclosure isintended to cover alternatives, modifications, and equivalents as may beincluded within the spirit and scope of the embodiments of the presentdisclosure as defined by the appended claims.

DETAILED DESCRIPTION

For purposes of the following description, it is to be understood thatembodiments provided by the present disclosure may assume variousalternative variations and step sequences, except where expresslyspecified to the contrary. Moreover, other than in the examples, orwhere otherwise indicated, all numbers expressing, for example,quantities of ingredients used in the specification and claims are to beunderstood as being modified in all instances by the term “about.”Accordingly, unless indicated to the contrary, the numerical parametersset forth in the following specification and attached claims areapproximations that may vary depending upon the desired properties to beobtained. At the very least, and not as an attempt to limit theapplication of the doctrine of equivalents to the scope of the claims,each numerical parameter should at least be construed in light of thenumber of reported significant digits and by applying ordinary roundingtechniques.

Notwithstanding that the numerical ranges and parameters setting forththe broad scope of the invention are approximations, the numericalvalues set forth in the specific examples are reported as precisely aspossible. Any numerical value, however, inherently contains certainerrors necessarily resulting from the standard variation found in theirrespective testing measurements.

Also, it should be understood that any numerical range recited herein isintended to include all sub-ranges encompassed therein. For example, arange of “1 to 10” is intended to include all sub-ranges between (andincluding) the recited minimum value of about 1 and the recited maximumvalue of about 10, that is, having a minimum value equal to or greaterthan about 1 and a maximum value of equal to or less than about 10.

A fiber-reinforced composite part can comprise one or more sections,where at least one of the one or more sections can comprise one or morealigned fiber portions; and each of the one or more aligned fiberportions independently comprises a plurality of co-aligned continuousfibers within a composition.

A section of a part refers to a portion of a part such as a segment of apart or a volume of a part. A portion refers to a region or volume of asection that comprises a different material than the material of anotherportion forming the section or that is derived from a different subunitthat the sections formed from. As disclosed herein, a section can befabricated by combining two or more subunits to form a section. Two ormore portions of a section can then be said to be derived from each ofthe two or more respective subunits.

A section can have one portion or more than one portions. Each of theone or more portions can have the same material or can have a differentmaterial. The one or more portions can be apparent in a cross-section ofa section.

A portion can comprise a composition. A composition can comprise amatrix material and one or more optional additives. A composition canalso comprise aligned fiber and/or non-aligned fiber. However, when acomposition is referred to as being the same as or different thananother composition, it is the matrix material and the one or moreoptional additives that are being referred to. For example, a firstcomposition and a second composition can both have the same or differentco-aligned continuous fiber, but have a different matrix material andoptional additives. The different matrix material and optional additivescan comprise different materials and/or different amounts of the samematerials.

A portion comprising co-aligned continuous fiber embedded within amatrix material is referred to as an aligned fiber portion.

A portion comprising non-aligned fiber embedded within a matrix materialis referred to as a non-aligned fiber portion.

An aligned fiber portion can also contain non-aligned fiber.

A portion can comprise a matrix material without co-aligned continuousfiber and without non-aligned fiber and is referred to as a non-fiberportion.

One or more aligned fiber portions, non-aligned fiber portions, and/ornon-fiber portions can be combined to form a section. In across-sectional view of a section, different regions or cross-sectionalareas will show the characteristics of the various portions forming thesection. For example, a left portion of the cross-section may show endsof co-aligned continuous fiber, an upper right portion can show randomlydispersed non-aligned fiber, and a lower right portion may not have anyfiber.

At least one of the sections can comprise one or more aligned fiberportions, and in some embodiments, two or more aligned fiber portions.The two or more aligned fiber portions may be adjacent each other or maybe separated from each other within a section. For example, two or morealigned fiber portions can be separated by non-aligned fiber portionsand/or non-fiber portions.

The two or more aligned fiber portions can comprise a first alignedfiber portion, where the plurality of co-aligned continuous fiberscomprises a first configuration; and a second aligned fiber portion,where the plurality of co-aligned continuous fibers comprises a secondconfiguration. A configuration can refer to the number of fibers, thedistribution of fibers within an aligned fiber portion, the type offibers such as the dimensions of the fibers and/or the materials formingthe fibers, or a combination of any of the foregoing.

For example, each of the first aligned fiber portion and the secondaligned fiber portion can have a substantially uniform distribution offibers or can have a substantially non-uniform distribution of fibersthroughout the respective aligned fiber portions.

The two or more aligned fiber portions can comprise a first alignedfiber portion, where the plurality of co-aligned continuous fiberscomprises a first configuration; and a second aligned fiber portion,where the plurality of co-aligned continuous fibers comprises a secondconfiguration; wherein the first configuration is substantiallydifferent than the second configuration.

For example, in a first configuration the co-aligned continuous fiberscan be uniformly distributed throughout the respective portion, and in asecond configuration the co-aligned continuous fibers can benon-uniformly distributed throughout the portion. In a uniformdistribution, any cross-sectional area of the aligned fiber portion canhave about the same number of fibers and/or about the same area of fiberto area of the composition in which the fibers are embedded. In anon-uniform distribution there can be, for example, more or less fiberin a cross-sectional area than in another section. For example, in anon-uniform configuration there can be relatively more fiber in a lowerarea, an upper area, a side area, a center area or a peripheral area,compared to another area of the non-aligned fiber portion.

The two or more aligned fiber portions can comprise a first alignedfiber portion comprising a first composition; and a second aligned fiberportion comprising a second composition, wherein the first compositionis substantially the same as the second composition. Compositions thatare substantially the same will have the same matrix material, the sameadditives, and will have approximately the same amount of each of thematrix material and additives, respectively. The amount of matrixmaterial and additives in terms of wt % refers to the wt % of the matrixmaterial and/or additive based on the total weight of the matrixmaterial and the additive. The wt % of aligned fiber and/or non-alignedfiber refers to the amount of fiber in a portion, based on the totalweight of the portion including the fiber, the matrix material, and anyoptional additives. The amount of a constituent in terms of vol % can bedetermined in a similar manner.

The two or more aligned fiber portions can comprise a first alignedfiber portion comprising a first composition; and a second aligned fiberportion comprising a second composition, where the first composition isdifferent than the second composition. For example, a first compositioncan have a polyethylene matrix material, and the second composition canhave a polypropylene matrix material. As another example, a firstcomposition can comprise light weight filler and the second compositioncan comprise a colorant. As another example, a first composition cancomprise 2 wt % of an adhesion promoter and the second composition cancomprise 5 wt % of an adhesion promoter, and otherwise have the samematrix materials and optional additives.

Each of the one or more sections of a composite part provided by thepresent disclosure can have one or more portions. For example, onesection can have one portion, another section can have two portions, andanother section can have three portions. Each of the portions indifferent sections can have the same composition or can have differentcompositions and each of the portions can have co-aligned continuousfiber, non-aligned fiber, or no fiber.

For example, the one or more sections can comprise a first sectioncomprising a first aligned fiber portion, wherein the first alignedfiber portion comprises a plurality of co-aligned continuous fibershaving a first configuration; and a second section comprising a secondaligned fiber portion, wherein the second aligned fiber portioncomprises a plurality of co-aligned continuous fibers having a secondconfiguration; wherein the first configuration is substantially the sameas the second configuration.

As another example, the one or more sections can comprise a firstsection comprising a first aligned fiber portion, wherein the firstaligned fiber portion comprises a plurality of co-aligned continuousfibers having a first configuration; and a second section comprising asecond aligned fiber portion, wherein the second aligned fiber portioncomprises a plurality of co-aligned continuous fibers having a secondconfiguration; wherein the first configuration is different than thesecond configuration.

Each section can comprise an aligned fiber portion, a non-aligned fiberportion, and/or a non-fiber portion. For example, a section can compriseone or more aligned fiber portions, one or more non-aligned fiberportions, and/or one or more non-fiber portions. A section cam containonly aligned fiber portions, only non-aligned fiber portions, or onlynon-fiber portions.

A section can contain one or more aligned fiber portions, one or morenon-aligned fiber portions, and no non-fiber portions.

A section can contain no aligned fiber portion, one or more non-alignedfiber portions, and one or more non-fiber portions.

A section can contain one or more aligned fiber portions, no non-alignedfiber portions, and one or more non-fiber portions.

A section can contain one or more aligned fiber portions and one or morenon-aligned fiber portions. The plurality of non-aligned fibers in thenon-aligned fiber portion can be oriented orthogonal to the alignment ofthe co-aligned continuous fiber of the aligned fiber portion. Theplurality of non-aligned fibers in the non-aligned fiber portion can beoriented parallel to the alignment of the co-aligned continuous fiber ofthe aligned fiber portion. The plurality of non-aligned fibers in thenon-aligned fiber portion can be oriented at an angle with respect tothe alignment of the co-aligned continuous fiber of the aligned fiberportion.

In aligned fiber portions comprising both co-aligned continuous fibersand non-aligned fibers, the non-aligned fibers can be entangled with theco-aligned continuous fibers. The non-aligned fibers can be uniformlydistributed throughout the aligned fiber portion, or can benon-uniformly distributed throughout the aligned fiber portion.

In sections having two or more portions, each of the two or moreportions can comprise an aligned fiber portion, a non-aligned fiberportion, or a non-fiber portion.

Each of the two or more aligned fiber portions independently cancomprise a first matrix material; each of the one or more non-alignedfiber portions can comprise a second matrix material; and each of one ormore non-fiber portions can comprise a third matrix material. The firstmatrix material and the second matrix material comprise the same matrixmaterial; the first matrix material and the third matrix materialcomprise the same matrix material; the second matrix material and thethird matrix material comprise the same matrix material; or each of thefirst matrix material, the second matrix material, and the third matrixmaterial comprise the same matrix material

In a section comprising portions having the same matrix material, thematrix material of one portion can be continuous with the matrixmaterial of another portion having the same matrix material. In acontinuous matrix material the matrix material from the two portions canform a single continuous material without any visually evidentinterface. A visually evident interface can result, for example, whenthere is an adhesion or bonding layer between the first and secondportions.

In other sections, the first matrix material and the second matrixmaterial can comprise a different matrix material; the first matrixmaterial and the third matrix material can comprise a different matrixmaterial; the second matrix material and the third matrix material cancomprise a different matrix material; or the first matrix material, thesecond matrix material, and the third matrix material can comprise adifferent matrix material.

The one or more portions of a section can comprise the same compositionor a different composition aside from whether the portions contain fiberor do not contain fiber. A composition will be the same as anothercomposition if it comprises the same matrix material and the sameadditives, wherein the additives are present in the amount, such as thesame wt % and/or vol %, based on the total weight or total volume,respectively, of the composition excluding the continuous and/ornon-aligned fiber. Portions having the same composition can have adifferent wt % and/or vol % of continuous fiber and/or non-alignedfiber.

A section can comprise only one or more aligned fiber portions, only oneor more non-aligned fiber portions, or only one or more non-fiberportions.

A section of a part can be linear, can have a bend, a curve, a complexshape, or a combination of any of the foregoing.

For a section having a bend, a bend can from an angle, for example,within a range of 5° to 179°, from 5° to 135°, or from 10° to 90°.

A section can incorporate one or more features to intended to provide afunctional attribute. Examples of functional attributes include, thermalconduction, electrical conduction, sensing, interconnection,communications, shielding, and a combination of any of the foregoing.

A section can incorporate, for example, an embedded wire, an embeddedelectrical conductor, an embedded thermal conductor, an embeddedwaveguide, an embedded optical fiber, an embedded sensor, an embeddedchannel, an embedded tube, or a combination of any of the foregoing.These elements can be embedded within the bulk of the section and/orembedded within a wall of the section. These elements can beincorporated into the filament used to fabricate a fiber-reinforced partprovided by the present disclosure and/or can be added to the partduring assembly of the layup.

Parts provided by the present disclosure can be fabricated bycompression molding one or more filaments. Thus, a fiber-reinforcedcomposite part provided by the present disclosure can comprise anysuitable matrix material that can be compression molded. Examples ofsuitable matrix materials include thermoplastics, thermosets, andceramics, and combinations of any of the foregoing.

Examples of suitable thermoplastics include polyethylene, polypropylene,polyvinyl chloride, polystyrene, acrylonitrile butadiene styrene,styrene butadiene styrene, styrene acrylonitrile, polyamide,polycarbonate, polymethylmethacrylate, polyoxymethylene (polyacetals),polyphenylene oxide, polyphenylene ether, polyethylene terephthalate,polybutylene terephthalate, polyetherimide, polyphenylene sulfide,ethylene tetrafluoroethylene, polyether ether ketone, liquid crystalpolymer, polytetrafluoroethylene, perfluoroalkoxy copolymer, fluorinatedethylene propylene, polyimide, polyamide, polybenzimidazole,polysulfone, polyaryletherketone, and thermoplastic polyurethane. Athermoplastic can be a thermoplastic elastomer such as polyurethaneelastomer, polyether ester block copolymer, styrenic block copolymer,polyolefin elastomer, polyether block amide, thermoplastic olefins,elastomeric alloys (TPE and TPV), thermoplastic polyurethanes,thermoplastic copolyesters, thermoplastic polyamides, and thermoplasticsilicone vulcanizate.

Examples of suitable thermosets include araldite, bakelites, epoxies,melamines, phenol/formaldehydes, polyesters, polyhexahydrotriazines,polyimides, polyisocyanates, polyureas, silicones, urea/formaldehydes,vinyl esters, phenolics, polycarbonates. Suitable thermosets can beprepared as a partially cured B-stage.

Examples of Suitable Ceramics Include Moldable Ceramics

Aligned fiber portions of a part can comprise a plurality of co-alignedcontinuous fibers embedded within a composition. The plurality ofco-aligned continuous fibers can be substantially uniformly distributedthroughout the aligned fiber portion, or can be non-uniformlydistributed throughout the aligned portion. Co-aligned continuous fibersrefers to fiber embedded within a composition that has been derived froma pultrusion.

Each of the plurality of co-aligned continuous fiber can have adiameter, for example, within a range from 1 μm to 100 μm, from 1 μm to90 μm, from 1 μm to 50 μm, from 5 μm to 40 μm, from 5 μm to 30 μm, from10 μm to 30 μm, or from 1 μm to 20 μm.

The plurality of co-aligned continuous fiber can comprise, for example,from 5 fibers to 80,000 fibers, from 10 fibers to 80,000 fibers, from100 fibers to 50,000 fibers, from 500 fibers to 40,000 fibers, or from1,000 fibers to 20,000 fibers.

A plurality of co-aligned continuous fibers can comprise silica, glass,carbon nanotubes, carbon, polymer, metal, ceramic, natural fiber,synthetic fibers, or a combination of any of the foregoing. A pluralityof co-aligned fiber can comprise carbon fibers.

A plurality of co-aligned continuous fiber can be in the form of a wire,a fabric, a ribbon, an extruded shape, a solid shape, a hollow shape, aperforated shape, a tube, a crystalline form, a non-crystalline form, anorganic shape, a roving, a sliver, a tow, a bundle, a spiral, or acombination of any of the foregoing.

An aligned fiber portion can comprise, for example from 1 wt % to 70 wt% co-aligned continuous fibers, from 5 wt % to 70 wt %, from 5 wt % to60 wt %, from 10 wt % to 50 wt %, from 10 wt % to 40 wt %, or from 15 wt% to 30 wt %, wherein wt % is based on the total weight of the alignedfiber portion.

An aligned fiber portion can comprise, for example from 1 vol % to 70vol % co-aligned continuous fibers, from 5 vol % to 70 vol %, from 5 vol% to 60 vol %, from 10 vol % to 50 vol %, from 10 vol % to 40 vol %, orfrom 15 vol % to 30 vol %, wherein vol % is based on the total volume ofthe aligned fiber portion.

The plurality of non-aligned fibers can comprise, for example, anaverage length less than 10 cm, less than 8 cm, less than 6 cm, lessthan 4 cm, less than 2 cm, less than 1 cm, or less than 0.5 cm.

The plurality of non-aligned fiber can comprise, for example, an averagelength within a range from 0.5 cm 10 cm, from 0.5 cm to 8 cm, from 0. 5cm to 6 cm, from 0.5 cm to 4 cm, from 0.5 cm to 2 cm, or from 1 cm to 2cm.

A non-aligned fiber portion can comprise, for example from 1 wt % to 70wt % non-aligned fibers, from 5 wt % to 70 wt %, from 5 wt % to 60 wt %,from 10 wt % to 50 wt %, from 10 wt % to 40 wt %, or from 15 wt % to 30wt %, where wt % is based on the total weight of the non-aligned fiberportion.

A non-aligned fiber portion can comprise, for example from 1 vol % to 70vol % non-aligned fibers, from 5 vol % to 70 vol %, from 5 vol % to 60vol %, from 10 vol % to 50 vol %, from 10 vol % to 40 vol %, or from 15vol % to 30 vol %, where vol % is based on the total volume of thenon-aligned fiber portion.

For aligned fiber portions comprising non-aligned fiber, the alignedfiber portion can comprise, for example, from 1 wt % to 70 wt % totalfibers, from 5 wt % to 70 wt %, from 5 wt % to 60 wt %, from 10 wt % to50 wt %, from 10 wt % to 40 wt %, or from 15 wt % to 30 wt %, where wt %is based on the total weight of the aligned fiber portion and the totalfiber includes the co-aligned continuous fiber and the non-alignedfiber.

For aligned fiber portions comprising non-aligned fiber, the alignedfiber portion can comprise, for example from 1 vol % to 70 vol % totalfibers, from vol % to 70 vol %, from 5 vol % to 60 vol %, from 10 vol %to 50 vol %, from 10 vol % to vol %, or from 15 vol % to 30 vol %, wherevol % is based on the total volume of the aligned fiber portion and thetotal fiber includes the co-aligned continuous fiber and the non-alignedfiber.

An aligned portion comprising aligned fiber and non-aligned fiber cancomprise, for example, less than 60 wt % non-aligned fiber, less than 50wt %, less than 40 wt %, less than 30 wt %, less than 20 wt %, less than10 wt % or less than 5 wt %, where wt % is based on the total weight ofthe aligned fiber and the non-aligned fiber. An aligned portioncomprising aligned fiber and non-aligned fiber can comprise from 1 wt %to 60 wt % non-aligned fiber, from 1 wt % to 50 wt %, from 1 wt % to 40wt %, from 1 wt % to 30 wt %, from 1 wt % to 20 wt % or from 1 wt % 10wt %, where wt % is based on the total weight of the aligned fiber andthe non-aligned fiber.

An aligned portion comprising aligned fiber and non-aligned fiber cancomprise, for example, less than 60 vol % non-aligned fiber, less than50 vol %, less than 40 vol %, less than 30 vol %, less than 20 vol %,less than 10 vol % or less than 5 vol %, where vol % is based on thetotal volume of the aligned fiber and the non-aligned fiber. An alignedportion comprising aligned fiber and non-aligned fiber can comprise from1 vol % to 60 vol % non-aligned fiber, from 1 vol % to 50 vol %, from 1vol % to 40 vol %, from 1 vol % to 30 vol %, from 1 vol % to 20 vol % orfrom 1 vol % 10 vol %, where vol % is based on the total volume of thealigned fiber and the non-aligned fiber.

A plurality of non-aligned fibers can comprise chopped fibers, milledfibers, or a combination thereof. Non-aligned fibers can include aplurality of non-aligned continuous fibers. A plurality of non-alignedcontinuous fibers can include, for example, fiber bundles, fiber weaves,twisted fibers, or a combination of any of the foregoing. Thenon-aligned fibers can comprise any of the materials suitable for use asfor co-aligned continuous fibers. Non-aligned fibers can comprise any ofthe form factors suitable for use as for co-aligned continuous fibers. Aplurality of non-aligned fibers can be in the form of pellets.

To fabricate a part, one or more filaments can be combined in differentsections to provide a layup, and the layup can be compression molded toprovide the completed part.

An example of the process for assembling a layup is shown in FIGS.1A-1F.

FIG. 1A shows examples of five (5) shaped filament subsections. Each ofthe shaped filament subsections can comprise substantially the samecomposition or one or more of the shaped filament subsections cancomprise a different composition. Each composition comprises a matrixmaterial. A composition can comprise fiber, which can include co-alignedcontinuous fibers, non-aligned fibers, or a combination thereof. Acomposition may not contain any co-aligned continuous fiber andnon-aligned fibers. A composition may also contain various additives.

The compositions for each of the various filament subunits can befabricated and selected to have certain properties depending on thelocation of the filament subunit within the layup. For example, sectionsof the part requiring high stiffness can comprise filament subunitscomprising a plurality of co-aligned continuous fiber. Filament subunitslocated on the outside of a part may be selected to enhance solventresistance, weatherability, aesthetics, and/or electrical and/or thermalconductivity. Other sections can be designed to increase, for example,tensile strength, compressive strength, flexural strength.

As shown in FIG. 1B the filament subunits can be assembled, layer bylayer, to build the layup.

In FIGS. 1B-1E filament subunits are combined to form the various layersof the layup. An assembled layup is shown in FIG. 1F.

The layup of filament subunits can be combined in a mold cavity toassemble the layup.

The filament subunits can be combined in a tray or a cavity that matchesthe mold cavity to provide a layup that can be transferred to the moldcavity. The filament subunits of this intermediate layup can be heldtogether, for example, with an adhesive.

FIG. 2A shows a view of a layup in a mold cavity. For a compressionmolded part, heat and pressure can be applied to cause the layup to flowand/or cure to form the finished part shown in FIG. 2B. For filamentscomprising thermoplastics, the temperature can be increased above themelt temperature of the thermoplastic to cause the thermoplastic to flowto fill the cavity. For thermosets, the thermosets are provided asB-stage materials and the application of heat and pressure can cause thethermoset to flow to fill the cavity and complete the curing reaction.For ceramics, the ceramics can be provided as materials that will flowand fully curing under a combination of heat and pressure. The moldcavity can include gates to reduce, redistribute and/or increase thecompositions at desired regions of a part.

Any suitable temperature and pressure can be used to compression moldthe part, which is in part determined by whether a thermoplastic, athermoset, or a ceramic is used and, for example, melt temperature ofthe thermoplastic, the thermoset chemistry, and the ceramic chemistry.

FIGS. 3A-3E show an example in which the part has a single U-shapedsection formed from three (3) filament subunits. FIG. 3A shows views ofthe three subunits that have profiles configured to mate with each ofthe other subunits. Each of the subunits can be combined with each ofthe other subunits as shown in FIGS. 3B-3D. The layup shown in FIG. 3Dcan be compression molded to provide the fabricated part shown in FIG.3E.

FIGS. 4A and 4B show photographs of a section of a part fabricatedaccording to methods provided by the present disclosure. FIGS. 4A and 4Bshow a section having a bend and the orientation of co-alignedcontinuous fiber through the bend (FIG. 4A) and the orientation ofco-aligned continuous fiber in a straight region of the section (FIG.4B).

Methods of fabricating a fiber-reinforced composite part can compriseproviding one or more filament subunits, where each of the one or morefilament subunits independently comprises a linear filament subunit, ashaped filament subunit, or a combination thereof; and at least one ofthe one or more filament subunits comprises a first compositioncomprising a plurality of co-aligned continuous fibers; placing the oneor more filament subunits into a mold cavity to form a layup; andcompression molding the layup to provide a fiber-reinforced compositepart.

A filament subunit includes a composition having matrix material andoptional additives. A filament can include a plurality of co-alignedcontinuous fiber and/or aligned fiber. Thus, a filament can comprise aco-aligned continuous fiber filament, a aligned fiber filament, or anon-fiber filament. Each of the co-aligned continuous fiber filament, anon-aligned fiber filament, or a non-fiber filament can be used to forman aligned fiber portion, a non-aligned fiber portion, or a non-fiberportion of a section of a part, respectively.

Suitable matrix materials include materials that can be molded. Moldingcan involve applying heat and/or pressure. Examples of suitable matrixmaterial includes thermoplastics, thermosets, and ceramics.

Suitable thermoplastics can be formed into filament subunits, can beassembled into a mold cavity, and can be formed into a part withapplication of heat and pressure. Suitable thermoplastics can have, forexample, a melt temperature above room temperature.

Suitable thermosets are able to form a B-stage that facilities handlingof the filament and assembly of filament subunits into a mold cavity. Acompleted part can be formed and the B-stage thermoset fully cured byapplying heat and pressure to a layup comprising thermoset filamentsubunits.

Suitable ceramics are also able to form a B-stage that faceplateshandling of the filament, assembly of the filament subunits into a moldcavity. The B-stage ceramic can be formed into a part by applying heatand pressure.

Filaments containing co-aligned continuous fiber can be formed, forexample, by pultrusion.

Filaments containing non-aligned non-continuous fiber and filamentsubmits without fiber can be formed, for example, using extrusion.

Filaments containing non-aligned continuous fiber can be formed, forexample, using extrusion.

A coating can be applied to the exterior surface of a filament. Acoating can be applied, for example, to the exterior surface foraesthetics, to enhance compatibility with other materials in a layup, toenhance adhesion to other materials in the layup, to facilitatemolecular bonding to other materials in the layup, or a combination ofany of the foregoing.

A filament can have any suitable cross-sectional profile. For example, afilament can have a simple circular or oval cross-sectional profile. Afilament can also have a specific cross-sectional profile that, incombination with other filaments having particular cross-sections, canbe combined to form a section of a part. An example in provided in FIGS.5A-5C. FIG. 5A shows a cross-sectional profile of a first filament, andFIG. 5B shows a cross-sectional profile of a second filament. Two of thefilaments shown in FIG. 5A can be combined with the filament shown inFIG. 5B to form a section having the cross-sectional profile shown inFIG. 5C. Heat and pressure can be applied the section shown in FIG. 5Cto provide a completed part.

A filament can be formed into a filament subunit. A filament subunit isan element that, along with other filament subunits, can be combined toform a layup.

A part can include one or more sections. Filament subunits can becombined to form the one or more sections of a part. A section of a partmay be formed from one or more filament subunits or portions of one ormore filament subunits.

Methods of fabricating high strength complex parts can compriseproviding a thermoplastic-impregnated fiber filament, forming thefilament into a shaped subunit, assembling shaped subunits into amolding cavity to provide a layup, and compression molding the layup toprovide a fiber-reinforced part. The methods can be adapted to fabricatehigh strength complex parts.

Thermoplastic-impregnated fiber filament can comprise fiber that isimpregnated with a thermoplastic material.

Thermoplastic-impregnated fiber filament comprises continuousunidirectional fiber impregnated with a thermoplastic.

Thermoplastic-impregnated fiber filament can be formed by pultrusion, aprocess by which fiber is pulled under tension through a die andimpregnated with a thermoplastic. In the process fiber can behomogeneously dispersed throughout the cross-sectional thickness of thepultrusion and fiber is aligned with the axis of the pultrusion. Thepultrusion process can be adapted to any suitable shape or partthickness. Furthermore, pultrusion can be adapted to form parts havingdifferent compositions along the length or cross-section of a part. Inother processes the fiber can comprise a bundle of fibers or severalbundles of fibers. A bundle of fibers can be referred to as a tow. A towis an untwisted bundle of continuous fibers. Thus, athermoplastic-impregnated fiber filament can comprise one or more tows.A tow can comprise, for example from 5 to 80,000 fibers, 1,000 to 50,000fibers, such as from 10 to 50,000 fibers, 1,000 to 40,000 fibers, from1,000 to 30,000 fibers, from 1,000 to 20,000 fibers or from 1,000 to5,000 fibers. A tow can have a diameter, for example, from about 0.5 mmto 3 mm

Each fiber can have any suitable dimension, which can be, for example,from about 3 μm to 20 μm to 20 μm, or from 5 μm to 10 μm for carbonfiber. Glass fiber can have a diameter, for example, from 5 μm to 50 μm.

A filament can comprise a single fiber, multiple fibers, or acombination thereof dispersed throughout a cross-section of a filament.The multiple fibers can be arranged into one or more fiber bundles. Afilament can comprise fibers that are separated or dispersed throughoutthe cross-sectional thickness of a tow such that for a givencross-sectional area the amount of fiber is about the same as anothercross-sectional area. Multiple filaments can be, for example, braided,woven, twisted, or a combination thereof.

To form a thermoplastic-impregnated fiber filament, one or more tows canbe impregnated with a thermoplastic using, for example, a pultrusionprocess. In a pultrusion process tow is pulled into a die under tensionand thermoplastic is injected into the die. The pultruded part can beshaped, cooled, and cut to length to provide thermoplastic-impregnatedfiber filament. Prior to entering the die, the fibers such as a tow canbe coated and/or treated with a sizing. A sizing includes chemicals thatbind the filaments together, reduces abrasion, facilitates impregnationwith the thermoplastic resin, and acts as a coupling agent that enhancescompatibility with the thermoplastic resin system.

During pultrusion the fibers forming a tow can become fully or partiallyseparated from the bundle to become uniformly coated with thermoplastic.

The pultruded parts, such as a pultruded thermoplastic-impregnated fiberfilament, can have any suitable shape and dimension for use fabricated ahigh strength part provided by the present disclosure. The pultrudedparts can have fiber substantially uniformly dispersed throughout thecross-sectional thickness of the part, or can be homogeneouslydistributed. For example, the fiber can be substantially disposed in thecross-sectional center of a part or substantially on one or more sidesof a part. The fiber can be oriented or substantially aligned with thelong axis of a pultrusion.

A thermoplastic-impregnated fiber filament can have a shape anddimensions that provide for the desired properties in the compressionmolded part, that facilitate layup in a mold cavity, and that facilitatecompression molding. For example, a thermoplastic-impregnated fiberfilament can have a cross-sectional shape that is substantially round,oval, square, rectangular, triangular, or a complex shape. Athermoplastic-impregnated fiber filament can have features thatfacilitate layup, alignment with other filaments in the mold cavity,and/or compression molding. Such features can take the form, forexample, of grooves or ridges.

Thermoplastic-impregnated fiber filament can have any suitable fiberreinforcement and can be impregnated with any suitable thermoplastic.The selection of the fiber and thermoplastic can depend on the desiredphysical properties of the compression molded part such as tensilestrength, flexural modulus, flexural strength and tensile modulus,solvent resistance, thermal resistance, density, thermal carbon,polyester, a liquid crystal polymer such as Vectran®, aramid fiber suchas Kevlar, cross-linked natural and synthetic rubbers, spandex fibers,segmented polyurethanes fibers such as Spandex®, cross-linkedpolyacrylate fiber such as anidex, and bi-constituent fiber of nylon andspandex.

Fibers can also include metal fibers.

A thermoplastic-impregnated fiber filament can have a single type offiber or multiple different types of fiber where the different types offiber can include different materials, thicknesses, or a combinationthereof.

A thermoplastic-impregnated fiber filament can have cross-sectionaldimension in which the height dimension is substantially similar to theheight dimension. For example, the height can be from 0.25 to 6 timesthe width, from 0.5 to 4 times the width, or from 1 times to 3 times thewidth. For example, the width can be from 0.25 to 6 times the height,from 0.5 to 4 times the height, or from 1 times to 3 times the height.Thermoplastic-impregnated fiber filament are not in the form tapes orsheets of material. The filament has dimensions that facilitate heatinga cross-section of the filament above the glass-transition temperatureof the thermoplastic and then cooling the softened thermoplastic belowthe glass-transition temperature to set a shape to the filament. It isdesirable that this heating and cooling process be carried out in lessthan 10 seconds, less than 5 seconds, less than 3 seconds, or less than1 second. Suitable dimensions and time can be influenced by the glasstransition of the thermoplastic and by the dimensions of a filament. Ingeneral, a filament can have a cross-sectional dimension, for example,less than 2 cm, less than 1.5 cm, less than 1 cm, less than 0.5 cm, orless than 0.25 cm.

Examples of suitable thermoplastics include polyethylene, polypropylene,polyvinyl chloride, polystyrene, acrylonitrile butadiene styrene,styrene butadiene styrene, styrene acrylonitrile, polyamide,polycarbonate, polymethylmethacrylate, polyoxymethylene (polyacetals),polyphenylene oxide, polyphenylene ether, polyethylene terephthalate,polybutylene terephthalate, polyetherimide, polyphenylene sulfide,ethylene tetrafluoroethylene, polyether ether ketone, liquid crystalpolymer, polytetrafluoroethylene, perfluoroalkoxy copolymer, fluorinatedethylene propylene, polyimide, polyamide, polybenzimidazole,polysulfone, polyaryletherketone, and thermoplastic polyurethane.

A thermoplastic can be a thermoplastic elastomer such as polyurethaneelastomer, polyether ester block copolymer, styrenic block copolymer,polyolefin elastomer, polyether block amide, thermoplastic olefins,elastomeric alloys (TPE and TPV), thermoplastic polyurethanes,thermoplastic copolyesters, thermoplastic polyamides, and thermoplasticsilicone vulcanizate.

The amount of fiber in a thermoplastic-impregnated fiber filament can bewithin a range, for example, from 10 wt % to 90 wt %, from 20 wt % to 80wt % from, 30 wt % to 70 wt %, from 40 wt % to 60 wt %, or from 60 wt %to 40 wt %, where wt % is based on the total weight of the filament. Forexample a thermoplastic-impregnated fiber filament can comprise from 40wt % to 60 wt % fiber, where wt % is based on the total weight of thefilament. The fiber in a thermoplastic-impregnated fiber filament can bewithin a range, for example, from 10 vol % to 90 vol %, from 20 vol % to80 vol % from, 30 vol % to 70 vol %, from 40 vol % to 60 vol %, or from60 vol % to 40 vol %, where vol % is based on the total volume of thefilament. For example a thermoplastic-impregnated fiber filament cancomprise from 40 vol % to 60 vol % fiber %, where vol % is based on thetotal volume of the filament. The amount of fiber and thermoplastic canbe determined, for example, by the desired strength, density, partcomplexity, and/or cost.

A filament can comprise a single fiber or a plurality of isolated fibersdisposed throughout the cross-sectional thickness of the filament.Individual fibers can be isolated, arranged in proximity to otherfibers, or twisted with respect to adjacent fibers.

The one or more fiber bundles can be disposed within the cross-sectionaldimension of the filament uniformly or non-uniformly. A fiber bundle canbe situated at the center of the filament. A fiber bundle can comprise,for example, from 1,000 fiber to 80,000 fibers. Individual fibersforming a fiber bundle can have a diameter less than 5 μm, less than 20μm, less than, less than 50 μm, or less than 100 μm. A fiber bundle canhave a cross-sectional diameter, for example from 0.25 mm to 10 cm.

The fibers can be substantially parallel through the length of afilament, can be twisted, or can vary position throughout the length ofa filament.

A fiber can comprise an inorganic fiber, an organic fiber, a ceramicfiber, a metal fiber, or a combination of any of the foregoing. Examplesof suitable fiber include, glass, silica, carbon, boron, silica carbide,ceramic, metal, organic materials, and synthetic fibers. Examples ofsuitable synthetic fibers include nylon, polyester, polypropylene,meta-aramid, para-aramid, polyphenylene sulfide, and rayon.

A fiber can have a solid core or can have a hollow core and/or cancomprise concentric layers of different materials

A fiber and the configuration of a fiber can be selected such that athermoplastic-impregnated fiber filament comprising the fiber can beshaped into a part and impart desirable properties to a finished partfabricated using the thermoplastic-impregnated fiber filament. Forexample, in small complex parts, with small-radius bends, smallerdiameter and/or flexible fibers that are flexible can be used.

A fiber can be a composite. For example, a fiber can comprise a corethat is coated with another material such as an electrically conductivematerial, an electrically insulating material, a thermally conductivematerial, a thermally insulating material, an impact resistant material,a lubricious material, or a smooth aesthetic material.

A fiber can have an exterior coating that enhances adhesion of the fiberto a thermoplastic.

A fiber can be selected to impart, for example, mechanical strength to afinished part, an electrical property to the finished part, a thermalproperty to the finished part, and/or a density to the finished part.

A filament can comprise any suitable thermoplastic. A thermoplastic canhave any suitable melt temperature appropriate for compression molding.A thermoplastic can have a melt temperature above the anticipated usetemperature of a part fabricated using the filament.

Thermoplastic-impregnated fiber filament can be prepared by co-extrudingfiber and thermoplastic using well-known methods such as pultrusion.

Thermoplastic-impregnated fiber filament can have any suitablecross-sectional shape and dimension. The cross-sectional shape anddimension of a filament can be selected based on the configuration ofthe fabricated part, the dimensions of the fabricated part, and/or thelayup of the filament within a mold cavity used to fabricate the part.

For example, a filament can have a round, oval, square, rectangular,triangular, or a complex cross-sectional shape.

A thermoplastic can be selected based on the thermal expansioncoefficient or solvent resistance. The thermal expansion coefficient ofa thermoplastic can be selected to tailor the expansion coefficient ofthe final composite material in combination with other compositeconstituents.

A fiber filament can be prepared by impregnating a plurality ofcontinuous fiber with a composition such as a thermoplastic composition,a thermoset composition, or a ceramic composition. In addition to amatrix material, a composition can comprise a filler. Suitable fillercan be selected to modify the mechanical, thermal, and/or electricalproperties of the cured part. A filler can be selected to reduce thedensity of the cured thermoplastic part. A filler can comprise aninorganic filler, an organic filler, or a combination thereof. Asuitable filler can include chopped fiber, particles, or a combinationthereof. The filler such as a chopped fiber can include sections ofchopped filament.

Examples of suitable fillers include inorganic fillers, such as carbonblack and calcium carbonate (CaCO₃), silica, polymer powders, andlightweight fillers. A composition can comprise from 5 wt % to 60 wt %of the filler or combination of fillers, from 10 wt % to 50 wt %, orfrom 20 wt % to 40 wt %, based on the total weight of the composition.Suitable lightweight fillers can have a specific gravity less than 1,less than 0.8, less than 0.6, less than 0.4, less than 0.2, less than0.1, or less than 0.05. Compositions provided by the present disclosuremay further include one or more colorants, thixotropic agents,accelerators, fire retardants, adhesion promoters, solvents, maskingagents, or a combination of any of the foregoing. As can be appreciated,fillers and additives employed in a composition may be selected so as tobe compatible with each other as well as the matrix material.

Compositions can include low density filler particles. A low densityparticles can have a specific gravity of no more than 0.7, no more than0.25, or no more than 0.1. Suitable lightweight filler particles canfall within two categories—microspheres and amorphous particles. Thespecific gravity of microspheres may range from 0.1 to 0.7 and include,for example, polystyrene foam, microspheres of polyacrylates andpolyolefins, and silica microspheres having particle sizes ranging from5 microns to 100 microns and a specific gravity of 0.25 (Eccospheres®).Other examples include alumina/silica microspheres having particle sizesin the range of 5 microns to 300 microns and a specific gravity of 0.7)(Fillite®), aluminum silicate microspheres having a specific gravity offrom 0.45 to 0.7 (Z-Light®), calcium carbonate-coated polyvinylidenecopolymer microspheres having a specific gravity of 0.13 (Dualite®6001AE), and calcium carbonate coated acrylonitrile copolymermicrospheres such as Dualite® E135, having an average particle size of40 μm and a density of 0.135 g/cc. Suitable fillers for decreasing thespecific gravity of the composition include, for example, hollowmicrospheres such as Expancel® microspheres (available from AkzoNobel)or Dualite® low density polymer microspheres (available from Henkel).

A low density filler can comprise less than 20 wt % of a composition,less than 15 wt %, less than 10 wt %, less than 5 wt %, less than 3 wt%, less than 2 wt % or less than 1 wt % of a composition, where wt % isbased on the total weight of the composition.

A filler can comprise an electrically and/or thermally conductivefiller. Examples of suitable electrically and/or thermally conductivefiller include nickel powders, nickel graphite, silver-coated glassspheres, carbon, graphite, metal fiber, and others.

A composition can comprise adhesion promoters. Adhesion promoters canenhance the adhesion of a thermoplastic to incorporated fiber. Anadhesion promoter may be present in amount from 0.1 wt % to 15 wt % of acomposition, less than 5 wt %, less than 2 wt %, or less than 1 wt %,based on the total dry weight of the composition. Examples of suitableadhesion promoters include phenolic resins, such as Methylon® phenolicresin, and organosilanes, such as epoxy, mercapto or amino functionalsilanes, such as Silquest® A-187 and Silquest® A-1100, available fromMomentive Performance Materials. Other useful adhesion promoters areknown.

A composition can comprise an additive. Examples of suitable additivesinclude plasticizers, pigments, surfactants, adhesion promoters,thixotropic agents, fire retardants, masking agents, and combinations ofany of the foregoing. When used, the additives may be present in acomposition in an amount ranging, for example, from 0 wt % to 60 wt %,such as from 1 wt % to 60 wt % or from 5 wt % to 20 wt %. Additives maybe present in a composition in an amount ranging from 25 wt % to 60 wt%, where wt % is based on the total weight of the composition.

Fiber filament can be applied as straight sections into a moldingcavity. Straight sections can be applied in any suitable configurationsuch as aligned in the same direction, orthogonal to each other and/oron top of other filaments.

A fiber filament includes a straight section of filament and a shapedfilament subunit. A straight filament subunit is a straight section ofthe fiber filament cut to a desired length for inserting into a moldcavity.

A fiber filament can be shaped into a shaped filament subunit. A shapedfilament subunit represents a structural component that can be insertedinto a mold cavity such as a compression mold cavity. Multiple filamentsubunits can be placed in a mold cavity in a predetermined configurationto assemble a molding layup. Filament subunits can be placed adjacentother filament subunits in the plane of the layup, over underlyingfilament subunits, and/or partly adjacent and partly overlying otherfilament subunits.

Fiber filament can be shaped into filament subunits for assembling themolding layup using any suitable method

For example, to shape a filament into a shaped filament subunit, an endof a continuous filament can be drawn into a shaping apparatus, shapedinto a predetermined two-dimensional and/or three dimensionalconfiguration, and the shaped portion of the filament can be separatedfrom the filament to provide a filament subunit.

An example of an apparatus configured to shape a filament into athermoplastic-impregnated fiber subunit is shown in FIG. 6.

FIG. 6 shows a schematic of a top view apparatus configured to advancefilament 602; in this using case rotating rollers 601. Filament 602 isadvanced into a shaping apparatus 603. In the shaping apparatus 603 agripper (not shown) secures the filament and holds the filament under aslight tension. To shape the filament, a retractable heating element 604is raised to heat the thermoplastic material of the filament above itsglass transition temperature. The retractable heating element 604 islowered into the shaping head 605. The gripper then moves the softenedfilament section against a cooling element (not shown) to form a bend inthe filament. The cooling element is configured to cool the filamentbelow the glass transition temperature of the thermoplastic to set theshape of the filament segment. The gripper releases the shaped filamentsection, additional filament is advanced into the shaping apparatus, thegripper secures the next section of filament and the shaping process isrepeated one or more times as appropriate based on the desiredconfiguration. When the filament subunit is shaped into a desiredconfiguration, the shaped filament subunit is separated from theadvancing filament to provide a shaped filament subunit. The shapedfilament subunit can be assembled into a layup.

As shown in FIG. 6 the shaped filament can be formed into a series of45° bends,

A shaped filament subunit can have one or more bends. The configurationand the dimensions of a bend can be selected based on the shape anddesired properties of the finished part. A bend can have any a suitablecurvature or radius. The section of shaped filament on either side of abend can be oriented at any suitable angle such as, for example, withina range from 5° to 175°, from 10° to 170°, from 15° to 165°, from 25° to155°, or from 45° to 135°.

A filament can be shaped into a two-dimensional shaped filament subunitin which the subunit segments are within a single plane.

A filament can be shaped to form a three-dimensional shaped filamentsubunit. This can be accomplished by the gripper moving the heatedfilament orthogonal to the direction of the bend before the gripperbrings the heated filament against the cooling block. The cooling blockcan include one or more features configured to control thethree-dimensional shape.

The shape of shaped filament subunits can be selected to provide desiredproperties to a compression molded part. Mechanical modeling such asfinite element analysis can be used to design a part to achieve certainproperties such as tensile and/or flexural strength. The orientationand/or concentration of fiber can be determined to provide the desiredproperties of the completed part. The part can then be deconstructedinto linear and shaped filament subunits that can be readily fabricatedand assembled into a mold cavity to provide a layup. In this way, overlycomplex shapes can be avoided and fiber reinforcement can beconcentrated in regions of the part to achieve optimum performance. Forexample, it can be desirable to have a higher concentration ofreinforcing fiber and corners and at the perimeter of a part to improverigidity. The shaped filament subunits can also be designed to minimizethe number of piece parts and thereby facilitate assembly efficiency.

Heat may be imparted to a filament by conduction, convection andradiation including thermal convection through air, thermal conductionthrough direct contact with the filament, by radiation like infraredradiation, by laser and/or by inductive heating. A filament can includean alloy filament of fiber to facilitate the ability to inductively heatthe matrix material such as a thermoplastic. The heating can besufficient to raise the temperature of the matrix material sufficientlyabove the melt temperature that the filament can be mechanicallydeformed into a desired shape.

A heating block can comprise a heat source like resistive heatingelements that employ heat transfer methods including conduction,convection and radiation and/or sources of electromagnetic radiationsuch as laser. A heating block can be open to the atmosphere or in aclosed or semi-closed heated chamber.

A heating block can have any suitable dimensions for heating thethermoplastic of a filament above the glass transition temperature. Thedimensions of the heating block can be selected based on the dimensionsof the filament and the glass transition temperature of thethermoplastic. It can be desirable that the thermoplastic filament beheated above the glass transition temperature throughout the thicknessof the filament, and that this be accomplished in a short time period tofacilitate high-volume manufacturing. At the same time, it can bedesirable that the temperature toward the surface of the filament not besufficiently above the melt temperature of the thermoplastic such as tocause the material to sag or otherwise deform before cooling.

FIG. 7 shows an example of a configuration of heating and coolingelements used to shape a thermoplastic-impregnated fiber filament. InFIG. 7 the heating element 701 is shown as a U-shaped heating block, theheating block can be configured to surround the filament 702 such thatthe heating block includes a mating heating block.

In addition to having at least one retractable section to enable theheated filament to be moved toward the cooling block, the heating blockcan include at least one section configured to contact the filament tofacilitate filament heating.

To facilitate high throughput production the advancing filament can beat least partially heated before entering the shaping apparatus. Thefilament can be partially heated above the melt temperature of thethermoplastic, for example, before the filament advancing apparatus, bythe filament advancing apparatus, or anywhere before the filament entersthe shaping apparatus.

The cooling element can comprise a heating block 703 configured to coolthe filament below its glass transition temperature and to shape thefilament section.

The temperature of the cooling block can be controlled by a fluidflowing through a one or more channels within the interior of thecooling block.

The cooling block can have an outer surface with a profile 704 forshaping a bend in the heated filament. The profile can have a desiredcurvature or radius.

A cooling block can comprise two or more cooling heads having differentshapes and/or profiles. The two or more cooling blocks can be mounted,for example, on a carousel configured to move a selected cooling headsin position to provide a desired shape to the heated filament.

Whereas the heating and cooling cycle in typical thermoplastic part cansignificantly impact the properties of the finished part such asbuilding stress into the part, in the present method, factors such asbuilt in stress are of less if of any importance. Because the shapedfilament subunits are used to build a layup that is then subjected totemperatures and pressures of compression molding that bring thetemperature of the thermoplastic above the glass transition temperature,any stress resulting from the shaping process is annealed away duringthe subsequent compression molding operation.

The surfaces of the heating and cooling elements that can come intocontact with the filament, and in particular the heated filament, can betreated to minimize or to prevent adhesion to the surfaces. For example,the material of the parts can be selected to minimize adhesion, or thesurfaces can be impregnated or coated with a material to minimizeadhesion such as treatment with a fluoropolymer.

After a filament section is shaped into a filament subunit, the filamentsubunit can be separated from the advancing filament using any suitablemethod such as, for example, by cutting. FIG. 6 shows a filament subunit606 having four (4) bends and a cutting mechanism 607 for separatingshaped filament subunit 606 from filament 602.

The separated shaped filament subunit can be further processed prior tolayup assembly. For example, the ends of the fiber can be cut to asuitable length, the subunit can be placed in a heated mold to form thefilament subunit into a three dimensional shape.

A fiber-reinforced filament can have a cross-sectional shape anddimension to substantially match the shape and dimension of the moldingcavity it will be placed in. Furthermore, a fiber-reinforced filamentcan have features that facilitate alignment with adjacent and/oroverlying layers of shaped filament. For example, a fiber-reinforcedfilament can have channels for tongue-and-groove alignment.

Finishing the filament subunit can comprise placing the filament subunitin a compression mold where the thermoplastic is brought about its melttemperature and further processed. After the filament subunit is shaped,a subsequent compression molding process can be used to tailor shape ofthe filament subunit, add features to facilitate alignment to thefilament subunit in the mold cavity, and/or add features for strengthenthe finished part. For example, the processing can be used to render thefilament subunit planar, add grooves and tongues for alignment, and/oradd through holes which can be used for alignment and/or for addingreinforcement such as a vertical wire at a bend or on either side of abend. The processing can be performed to planarize the shaped filamentsubunit to facilitate layup assembly. In this operation, a shapedfilament subunit can be compressed between heated platens.

In a production environment, the method of shaping filament can comprisemultiple nodes in which the same or different shaping processes canoperate simultaneously to harmonize filament shaping rate withcompression molding rate.

The next step in forming a complex fiber-reinforced part is to placemultiple filament subunits into a mold cavity.

A mold cavity is configured in substantially the shape of the finishedpart. The mold cavity is used to compression mold the part and the layuprefers to the stack of materials such as the stack of linear and/orshaped filament subunits inserted into the mold cavity prior tocompression molding. Frequently, compression molding is performed usingthermoset materials that can be exothermic. In the disclosed methods,because a thermoplastic material is employed, the compression mold isheated such that the thermoplastic can be heated above the melttemperature to enable the thermoplastic in the filament to flow andconform to the mold cavity to provide the shape of the finished part.

The mold cavity can be made of any suitable material such as P-20 moldsteel.

To assembly the layup a plurality of filament subunits are selected andplaced into the mold cavity into a predetermined configuration. Aplurality of filament subunits are provided, which when placed in themold cavity to form the filament layup, are subsequently heated andcompressed using compression molding, cooled, and then ejected from themold to provide a part.

The filament subunits can be assembled on top of other filamentsubunits, adjacent other filament subunits, and/or within the same planeas another filament subunit. For any given cross-section of a mold therewill be two or more filament subunits stacked on top of each other. Thisconfiguration can impart increased strength to the finished part andfacilitates the use of fiber-reinforced filaments with smallercross-sectional dimensions as appropriate for forming complex parts.

Individual filament subunits can be placed into a mold cavity usingpick-and-place equipment. The filament subunits can have variouscross-sectional dimensions and/or shapes depending, for example, on thedimensions of the cavity and/or the position of a filament subunitwithin the layup. Examples of various layup configurations are shown inFIGS. 8A-8F. FIG. 8A shows cross-sections of various filament subunitshaving various profiles fit into various cavities. The individualfilament subunits can have dimensions that approximately fill thevarious dimensions of the cavity and can comprise various materials assuitable to meet the performance requirements of the completed part.FIG. 8B shows another cross-sectional view of a filament subunit layup.FIG. 8C shows a view of a filament layup in which the filaments subunitson the left have one property and the filament subunits on the righthave a different property. For example, the filament subunits on theright can be selected to increase the thermal conduction of the innerportion of the completed part and the filament subunits on the right canbe selected to increase thermal insulation. The filament subunits on theright can have a certain color or include an additive such as wood fiberto enhance the aesthetics of the outward-facing surface. FIG. 8D showsan arrangement similar to that of FIG. 8C, but with the addition of anembedded element identified by the small-diameter feature. This elementcan be, for example, a wire, a channel, a sensor, an optical fiber, orother element. For example, as a resistive wire, heat could be providedto the part. Alternatively, as a cooling channel, a liquid or gas can bepassed through the channel to cool the part. FIG. 8E shows a view, suchas a top view of a bicycle helmet, in which filament subunits are laidinto the compression mold at strategic locations to improve the overallstrength of the bicycle helmet. The continuous fiber can provide asecondary reinforcement when the mesh-composite shell fractures andthereby reduce the impact injury due to fragments. The filament subunitsare design to the shape of the mold. FIG. 8F shows a profile of anoval-shaped part with co-aligned continuous fiber regions indicated bythe stippled circles and embedded wire represented by the solid circles.Such high strength structural members can be used, for example, inbicycle frames, drones, UAV arms, robotics, buildings, lighting,motorized vehicle frames, prosthetics, or medical devices. The wires canbe used as antennas, controls, interconnects, sensors, or strain gauges.

The methods of manufacturing unidirectional fiber composite partsprovided by the present disclosure combines the advantages of methodsused for automated fiber placements, automated tape layup and additivemanufacturing, and compression molding. Automated fiber layup is capableof depositing fibers at high speed to produce convex parts with limitedintentional alignment and shaping of continuous fibers. The presentmethod avoid disadvantages of automated fiber placement associated withthe limited ability to fabricate complex parts and adhesion betweeninterlayers. Automated tape layup and additive manufacturing can be usedto intentional align and shape continuous fibers but the process isslow, expensive and can be restricted to certain geometries. Compressionmolding provide high part integrity and interlayer adhesion, can beautomated fro high speed and high volume production, and can provideexcellent surface finishes, maintain tight tolerance, is repeatable, andcan be adapted to many material systems. On the other hand, typicalcompression molding processes are not amenable to the intentionalalignment and shaping of fibers.

The shape, dimensions, and materials forming the layup can be selectedto provide a finished part having a desired property.

The design of the layup can be established based on mechanical modelingof the fabricated part. For example, finite element analysis can be usedto model the mechanical properties of a fabricated part based on theconfiguration of the filament subunits, fiber, thermoplastic, and othermaterials used in the layup.

One of the objectives of using co-aligned continuous fiber filament isto improve the flexural strength of a complex part compared to similarlyshaped parts fabricated using other thermoplastic-based methods,thermoset-based methods, or ceramic-based methods.

One of the objectives of using a co-aligned continuous fiber filament isto reduce the weight and/or size a complex part compared to similarlyshaped parts fabricated using other manufacturing methods such as bymachining metal parts

The layup can also include shaped subunits that do not contain fiber.

The layup can also include chopped filament. The chopped filament cancomprise the same material as the continuous fiber-reinforced filamentand/or a different fiber and/or matrix material than that of thecontinuous fiber-reinforced filament.

The filament sections in a layup can be selected to provide selectedproperties in different regions of a part.

For example, for parts in which it is desired that certain regions arethermally conductive and others thermally non-conductive, the selectfilament subunits can be selected accordingly. An example is shown inFIG. 8C in which the filament subunits on the left are thermallyinsulating and can include glass fiber, and the filament subunits on theright are thermally conductive and can include graphite.

Thus, for a cross-sectional profile of a part the filament subunits canbe selected such that one or more properties are different across or incertain regions of the profile. Furthermore, the filament subunits canbe selected such that the part has different properties in differentsections of the part.

A layup can also include other elements such as wire, optical fiber,channel, and tubing. These elements can be used for heating, cooling,pneumatics, hydraulics, sensing, interconnection, signal transmission.The connectorized elements can be fixture into the mold for precisealignment and streamlined production when assembling the layup.

The layup can be assembled in a holding tray. The filament subunits canbe held together by melting the thermoplastic resin and tack bondingoverlying and/or adjacent filament segments. The layups in the holdingtray can be transferred to a mold cavity.

After transferring the layup to the compression molding cavity, moltenthermoplastic resin can be added to the cavity to reduce or to eliminatevoids.

A mold cavity can include appropriately located sprues to facilitateeven compression.

In a production environment, a compression mold can comprise multiplecavities in which the filament layups can be molded into a completedpart.

The materials used in the layup can be selected for compatibility. Forexample, thermoplastics used in the layup can be selected to have asimilar melt temperature and/or similar thermoplastic families can beselected to improve intermolecular diffusion.

When dissimilar materials can be used there the interfaces can beincompatible such as having poor interfacial bonding strength that cancause a part to delaminate.

To avoid or minimize interface incompatibility and pullout materials andfilaments used in a layup can have surface treatments to facilitateinterfacial bonding. These can include primers or interlayer coatingsthat are well known in the coating industry. The thermoplastics cancomprise adhesion promoters that facilitate bonding to the fiber and/orto other materials within the layup.

In addition to the fiber filament, a layup can include filament (withoutfiber) and/or pellets comprising the matrix material. The filament cancomprise segments of thermoplastic formed into subunits. Pellets, beads,or other shapes can comprise the same or similar t composition as in thefiber filament. Pellets can comprise a filler such as an organic filler,an inorganic filler, or a combination therefore, which can be thermallyconductive, electrically conductive, or lightweight. A pelletcomposition can comprise adhesion promoters and additives asappropriate.

A layup can also include fiber filament extruded into the mold cavity.Fiber filament can be extruded using an additive manufacturing apparatusfitted with a heated nozzle and the molten thermoplastic fiber filamentdeposited into the mold cavity in a desired configuration.

Additional fiber-reinforced segments can be inserted into the layup suchthat the fiber orientation is orthogonal to the long fiber segments inthe set up. The orthogonal fibers can be situated in regions of the partwhere increased structural integrity and resistance to delamination isdesired. Certain part loading scenarios might require fiber orientationbetween that of the aforementioned long fiber segments and orthogonalreinforcements or alternatively, a combination of orientations atdifferent sections of the part might be required for complex loadingscenarios.

It can be desirable to select the dimensions and cross-sectional profileof overlying filament subunits to prevent or minimize the potential foran overlying filament to slip past into or past an underlying filamentsubunit or section of a filament subunit during compression molding.

A layup can comprise vertical reinforcing elements such as verticalmetal segments

A layup can comprise embedded wire, optical fiber, sensors, channels, ora combination of any of the foregoing. These and other elements can beused, for example, for interconnection, thermal control, sensing, and/orcommunications.

Compression molding is widely used with thermoset materials. Incompression molding the charge or as applicable here, the layup, isheated and compressed under high pressure to form a part.

For purposes of the present invention the mold cavity can be heatedabove the melt temperature of the thermoplastics used in the layup andpressure applied to cause the thermoplastic and impregnated fiber toflow and fill the cavity. The mold is then cooled to below the melttemperature and the part removed from the cavity.

The cycle time of each of the processes, heating, application ofpressure, and cooling can be selected to optimize manufacturingthroughput and to optimize the properties of the finished part. Forexample, the temperature and pressure and time can be selected to ensureadequate flow of the material and redistribution of the fibers, and thecooling temperature and time can be selected, for example, to minimizestress in the finished part.

An objective of the invention is to fabricate complex parts having ahigher tensile strength. The method can be used, for example, tofabricate high strength thermoplastic parts that can be used to replacemetal parts.

A fiber-reinforced part provided by the present disclosure has longsegments of fiber oriented parallel to or roughly following a surfacehaving the largest dimension of the part.

A fiber-reinforced composite part can comprise a plurality of co-alignedfiber segments embedded within a thermoplastic resin.

In cross-section, the part can have multiple fiber segments stacked ontop of each other. In the orthogonal cross-section, the part will showlong segments of fiber bundles.

For example, a fiber-reinforced composite part can comprise a firstdimension and a second dimension; wherein the second dimension isorthogonal to the first dimension; wherein a first cross-section of thecomposite part parallel to the first dimension comprises one or moresubstantially parallel fibers; and wherein a second cross-section of thecomposite part parallel to the second dimension comprises end sectionsof one or more fibers. In certain parts a section containing fibers canhave a plurality of fibers distributed substantially homogeneouslythroughout the cross-section of the part.

A fiber-reinforced part can have a specific gravity, for example, from1.0 to 1.5, from 1.1 to 1.5, from 1.2 to 1.5, or from 1.2 to 1.4.

A fiber-reinforced part can have a tensile strength from 100 MPa to 600MPa, from 100 MPa to 400 MPa, from 150 MPa to 350 MPa, or from 200 MPato 300 MPa.

A fiber-reinforced part can have a tensile modulus, for example, from10,000 MPa to 70,000 MPa, from 15,000 MPa to 60,000 MPa, from 20,000 MPato 55,000 MPa, from 25,000 MPa to 50 MPa, or from 30 MPa to 45,000 MPa.

Methods and apparatus provided by the present disclosure can be used tofabricate complex parts having high mechanical strength.

FIG. 9 shows a stress profile of a part fabricated using methodsaccording to the present disclosure. FIG. 9 shows the stress profiled ofa part calculated using finite element analysis. The arrangement ofco-aligned continuous fiber in the part is shown by the grey lines. Thefibers are aligned along loading paths within the part and therebyincrease the strength and stiffness of the part. The strength of thepart is greater than that of a comparable metal part and lower in weightthan a metal part. This is accomplished while using the designflexibility and high throughput of compression molding.

Parts fabricated using methods and apparatus provided by the presentdisclosure can be used, for example, for replacing metal parts, inaerospace applications, consumer electronics, sporting equipment,vehicles, surgical implants, communications devices, portable devices,medical devices, robotics, industrial equipment and prosthetics.

The methods and apparatus are particularly useful for fabricating small,complex parts and geometries with open lattice-like structures.

A filament can be shaped using a number of methods, which in part can bedetermined by the configuration of the shaped filament subunit.

A method of fabricating a shaped filament subunit can comprise securinga section of one or more filaments; and shaping the one or more filamentsections to provide one or more shaped filament subunits.

Tension can be applied to the filament during shaping.

Before a filament is shaped, heat can be applied to at least a portionof the filament section. The heat can soften the filament section suchthat it can be formed into a desired shape. After the heated filamentsection is shaped, the heated filament section can be cooled. Coolingcan involve allowing the heat to dissipate, applying a cooling blockdirectly to the heated and shaped section, or forcing cold air over theheated and shaped section. Cooling can proceed on an appropriate timescale and can include progressively cooling the heated and shapedfilament section.

Shaping can include combining two or more filaments into a singlefilament than can then be shaped. The each of the one or more filamentsto be combined can independently comprise an aligned fiber filaments, anon-aligned fiber filaments, or a non-fiber filament.

A method of fabricating a shaped filament subunit can involvesimultaneously shaping multiple filaments to provide multiple respectivefilament subunits. The same operation(s) that are sued to fabricated asingle filament subunit can be used to fabricate multiple filamentsubunits.

Other methods of shaping a filament subunit include depositing afilament into cavity having the shape of a desired filament subunit.Shaping can comprise applying a filament onto a surface in the shape ofa desired filament subunit.

During the process of shaping, a part can be embedded into the bulk ofthe shaped filament, embedded in a surface of a shaped filament, orapplied to the surface of a shaped filament. The parts can add strengthto a part fabricated using the shaped filament, add a function such asconnectors to a part fabricated using the shaped filament. Suitableparts include, for example, part comprises a pin, an insert, a standoff,an anchor, a shaft, a tube, a connector, a fabric, a unidirectionalprepreg, a bidirectional prepreg, or a combination of any of theforegoing. The part can be introduced into the bulk and/or surface ofthe shaped filament during shaping when the filament matrix material ispliable. For example, during shaping, a filament is can be bent around apart, which then can become incorporated into the shaped filament.

An alternative way of fabricating a part from filament comprisessecuring one or more filaments to a first anchor; and extending the oneor more filaments in a direction away from the first anchor to providethe part. As the one or more filaments is drawn away from the anchor theone or more filaments can be laid down in a desired shape. As the one ormore filaments is drawn away from the first anchor the extendingfilaments can be secured to one or more second anchors and the one ormore filaments can be extended by drawing the one or more filaments awayfrom the one or more second anchors.

Intersections between the one or more filaments can be joined such as beapplying heat and pressure to the intersections, and/or by depositing areinforcing composition at the intersections, wherein the reinforcingcomposition can comprise chopped fiber, milled fiber, or a combinationthereof.

ASPECTS OF THE INVENTION

Aspect 1. A fiber-reinforced composite part, comprising one or moresections, wherein, at least one of the one or more sections comprisestwo or more aligned fiber portions; and each of the two or more alignedfiber portions independently comprises a plurality of co-alignedcontinuous fibers within a composition.

Aspect 2. The fiber-reinforced composite part of aspect 1, wherein eachof the compositions independently comprises a matrix material, whereinthe matrix material comprises a thermoplastic, thermoset, or a ceramic.

Aspect 3. The fiber-reinforced composite part of any one of aspects 1 to2, wherein the two or more aligned fiber portions comprise: a firstaligned fiber portion, wherein the plurality of co-aligned continuousfibers comprises a first configuration; and a second aligned fiberportion, wherein the plurality of co-aligned continuous fibers comprisesa second configuration; wherein the first configuration is substantiallythe same as the second configuration.

Aspect 4. The fiber-reinforced composite part of any one of aspects 1 to3, wherein the two or more aligned fiber portions comprise: a firstaligned fiber portion, wherein the plurality of co-aligned continuousfibers comprises a first configuration; and a second aligned fiberportion, wherein the plurality of co-aligned continuous fibers comprisesa second configuration; wherein the first configuration is substantiallydifferent than the second configuration.

Aspect 5. The fiber-reinforced composite part of any one of aspects 1 to4, wherein the two or more aligned fiber portions comprise: a firstaligned fiber portion comprising a first composition; and a secondaligned fiber portion comprising a second composition, wherein the firstcomposition is substantially the same as the second composition.

Aspect 6. The fiber-reinforced composite part of any one of aspects 1 to5, wherein the two or more aligned fiber portions comprise: a firstaligned fiber portion comprising a first composition; and a secondaligned fiber portion comprising a second composition, wherein the firstcomposition is different than the second composition.

Aspect 7. The fiber-reinforced composite part of any one of aspects 1 to6, wherein the one or more sections comprise: a first section comprisinga first aligned fiber portion, wherein the first aligned fiber portioncomprises a plurality of co-aligned continuous fibers having a firstconfiguration; and a second section comprising a second aligned fiberportion, wherein the second aligned fiber portion comprises a pluralityof co-aligned continuous fibers having a second configuration; whereinthe first configuration is substantially the same as the secondconfiguration.

Aspect 8. The fiber-reinforced composite part of any one of aspects 1 to7, wherein the one or more sections comprise: a first section comprisinga first aligned fiber portion, wherein the first aligned fiber portioncomprises a plurality of co-aligned continuous fibers having a firstconfiguration; and a second section comprising a second aligned fiberportion, wherein the second aligned fiber portion comprises a pluralityof co-aligned continuous fibers having a second configuration; whereinthe first configuration is different than the second configuration.

Aspect 9. The fiber-reinforced composite part of any one of aspects 1 to8, wherein at least one of the two or more aligned fiber portionscomprises a plurality of co-aligned continuous fibers disposedsubstantially uniformly throughout the aligned fiber portion.

Aspect 10. The fiber-reinforced composite part of any one of aspects 1to 9, wherein at least one of the two or more aligned fiber portionscomprises from 10 wt % to 70 wt % fibers, wherein wt % is based on thetotal weight of the at least one aligned fiber portion.

Aspect 11. The fiber-reinforced composite part of any one of aspects 1to 10, wherein at least one of the two or more aligned fiber portionscomprises from 10 vol % to 70 vol % fibers, wherein vol % is based onthe total volume of the at least one aligned fiber portion.

Aspect 12. The fiber-reinforced composite part of any one of aspects 1to 11, wherein, each of the compositions independently comprises amatrix material; and the matrix material of each of the two or morealigned fiber portions is continuous with the matrix material of each ofthe other two or more aligned fiber portions.

Aspect 13. The fiber-reinforced composite part of any one of aspects 1to 12, wherein, each of the at least one of the one or more sectionsfurther comprises one or more non-fiber portions; and each of the one ormore non-fiber portions comprises a composition without co-alignedcontinuous fibers and without non-aligned fibers.

Aspect 14. The fiber-reinforced composite part of any one of aspects 1to 13, wherein, each of the at least one of the one or more sectionscomprises one or more non-aligned fiber portions; and each of the one ormore non-aligned fiber portions comprises a composition comprising aplurality of non-aligned fibers.

Aspect 15. The fiber-reinforced composite part of aspect 14, wherein theplurality of non-aligned fibers comprises a length less than 10 cm.

Aspect 16. The fiber-reinforced composite part of any one of aspects 14to 15, wherein the plurality of non-aligned fibers are orientedsubstantially orthogonal to an alignment of the co-aligned continuousfibers in an aligned fiber portion.

Aspect 17. The fiber-reinforced composite part of any one of aspects 14to 16, wherein the plurality of non-aligned fibers comprises choppedfibers, milled fibers, or a combination thereof.

Aspect 18. The fiber-reinforced composite part of any one of aspects 14to 17, wherein the plurality of non-aligned fibers are in the form ofpellets.

Aspect 19. The fiber-reinforced composite part of any one of aspects 1to 18, wherein at least one aligned fiber portion further comprises aplurality of non-aligned fibers.

Aspect 20. The fiber-reinforced composite part of aspect 19, wherein theplurality of non-aligned fibers comprises a length less than 10 cm.

Aspect 21. The fiber-reinforced composite part of any one of aspects 19to 20, wherein the plurality of non-aligned fibers are orientedsubstantially orthogonal to an alignment of the co-aligned continuousfibers in an aligned fiber portion.

Aspect 22. The fiber-reinforced composite part of any one of aspects 19to 21, wherein the plurality of non-aligned fibers comprise choppedfibers, milled fibers, or a combination thereof.

Aspect 23. The fiber-reinforced composite part of any one of aspects 19to 22, wherein the plurality of non-aligned fibers are in the form ofpellets.

Aspect 24. The fiber-reinforced composite part of any one of aspects 19to 23, wherein the plurality of non-aligned fibers are entangled amongthe plurality of co-aligned continuous fibers.

Aspect 25. The fiber-reinforced composite part of any one of aspects 1to 24, wherein the one or more sections comprising two or more alignedfiber portions further comprises: one or more non-aligned fiber portionscomprising non-aligned fiber; one or more non-fiber portions withoutco-aligned continuous fiber and without non-aligned fiber; or both oneor more non-aligned fiber portions and one or more non-fiber portions.

Aspect 26. The fiber-reinforced composite part of aspect 25, wherein,each of the two or more aligned fiber portions independently comprises afirst matrix material; each of the one or more non-aligned fiberportions comprises a second matrix material; and each of the one or morenon-fiber portions comprises a third matrix material.

Aspect 27. The fiber-reinforced composite part of aspect 26, wherein,the first matrix material and the second matrix material comprise thesame matrix material; the first matrix material and the third matrixmaterial comprise the same matrix material; the second matrix materialand the third matrix material comprise the same matrix material; or eachof the first matrix material, the second matrix material, and the thirdmatrix material comprise the same matrix material.

Aspect 28. The fiber-reinforced composite part of aspect 26, whereineach of the first matrix material, the second matrix material, and thethird matrix material is continuous with each of the other matrixmaterials.

Aspect 29. The fiber-reinforced composite part of aspect 25, wherein,the first matrix material and the second matrix material comprise adifferent matrix material; the first matrix material and the thirdmatrix material comprise a different matrix material; the second matrixmaterial and the third matrix material comprise a different matrixmaterial; or the first matrix material, the second matrix material, andthe third matrix material comprise a different matrix material.

Aspect 30. The fiber-reinforced composite part of aspect 25, whereineach of the first matrix material, the second matrix material, and thethird matrix material is continuous with each of the other matrixmaterials.

Aspect 31. The fiber-reinforced composite part of any one of aspects 1to 31, wherein, each of the two or more aligned fiber portionsindependently comprise a first composition; each of the one or morenon-aligned fiber portions comprises a second composition; and each ofthe one or more non-fiber portions comprises a third composition,wherein each composition comprises a matrix material and one or moreadditives.

Aspect 32. The fiber-reinforced composite part of aspect 31, wherein,the first composition and the second composition comprise the samecomposition; the first composition and the third composition comprisethe same composition; the second composition and the third compositioncomprise the same composition; or each of the first composition thesecond composition, and the third composition comprise the samecomposition.

Aspect 33. The fiber-reinforced composite part of aspect 31, wherein,the first composition and the second composition comprise a differentcomposition; the first composition and the third composition comprise adifferent composition; the second composition and the third compositioncomprise a different composition; or each of the first composition, thesecond composition, and the third composition comprise a differentcomposition.

Aspect 34. The fiber-reinforced composite part of aspect 31, whereineach of the first composition, the second composition, and the thirdcomposition is continuous with each of the other compositions.

Aspect 35. The fiber-reinforced composite part of any one of aspects 1to 35, wherein at least one of the one or more sections does notcomprise a co-aligned continuous fibers and does not comprisenon-aligned fibers.

Aspect 36. The fiber-reinforced composite part of any one of aspects 1to 36, wherein at least one of the one or more sections comprisesnon-aligned fibers.

Aspect 37. The fiber-reinforced composite part of any one of aspects 1to 37, wherein at least one of the one or more sections does notcomprise co-aligned continuous fibers.

Aspect 38. The fiber-reinforced composite part of any one of aspects 1to 38, wherein the plurality of co-aligned continuous fibers comprisesfrom 5 fibers to 80,000 fibers.

Aspect 39. The fiber-reinforced composite part of any one of aspects 1to 39, wherein the plurality of co-aligned continuous fibers comprisessilica, glass, carbon nanotubes, carbon, polymer, metal, ceramic,natural fiber, synthetic fibers, or a combination of any of theforegoing.

Aspect 40. The fiber-reinforced composite part of any one of aspects 1to 40, wherein the plurality of co-aligned continuous fibers is in theform of a wire, a fabric, a ribbon, an extruded shape, a solid shape, ahollow shape, a perforated shape, a tube, a crystalline form, anon-crystalline form, an organic shape, a roving, a sliver, a tow, abundle, a spiral, or a combination of any of the foregoing.

Aspect 41. The fiber-reinforced composite part of any one of aspects 1to 41, wherein at least one of the one or more sections comprises atleast one linear portion, at least one bend, or a combination thereof.

Aspect 42. The fiber-reinforced composite part of aspect 41, wherein theat least one bend forms an angle within a range from 5° to 179°.

Aspect 43. The fiber-reinforced composite part of any one of aspects 1to 42, wherein at least one of the one or more sections comprises anembedded wire, an embedded electrical conductor, an embedded thermalconductor, an embedded waveguide, an embedded optical fiber, an embeddedsensor, an embedded channel, an embedded tube, or a combination of anyof the foregoing.

Aspect 44. A method of fabricating a fiber-reinforced composite partcomprising; providing one or more filament subunits, wherein, each ofthe one or more filament subunits independently comprises a linearfilament subunit, a shaped filament subunit, or a combination thereof;and at least one of the one or more filament subunits comprises a firstcomposition and a plurality of co-aligned continuous fibers; placing theone or more filament subunits into a mold cavity to form a layup; andcompression molding the layup to provide a fiber-reinforced compositepart.

Aspect 45. The method of aspect 44, wherein the one or more filamentsubunits further comprise: a filament subunit comprising a secondcomposition and a plurality of non-aligned fibers; a filament subunitcomprises a third composition and does not comprise a co-alignedcontinuous fibers and does not comprise non-aligned fibers; or acombination thereof.

Aspect 46. The method of aspect 45, wherein, each of the firstcomposition, the second composition; and the third composition comprisessubstantially the same composition.

Aspect 47. The method of aspect 45, wherein, each of the firstcomposition and the second composition comprise the same matrixmaterial; the first composition and the third composition comprise thesame matrix material; the second composition and the third compositioncomprise the same matrix material; or the first composition, the secondcomposition, and the third composition comprise the same matrixmaterial.

Aspect 48. The method of aspect 45, wherein, each of the firstcomposition and the second composition comprise a different matrixmaterial; the first composition and the third composition comprise adifferent matrix material; the second composition and the thirdcomposition comprise a different matrix material; or the firstcomposition, the second composition, and the third composition comprisea different matrix material.

Aspect 49. The method of any one of aspects 44 to 48, wherein placingthe one or more filament subunits into a mold cavity comprises placingthe one or more filament subunits into a holding tray to form anassembly layup, and transferring the assembly layup to the mold cavity.

Aspect 50. The method of any one of aspects 44 to 49, wherein placingthe one or more filament subunits into a mold cavity comprises placingthe one or more filament subunits onto an underlying filament subunit,adjacent a filament subunit, or a combination thereof.

Aspect 51. The method of any one of aspects 44 to 50, wherein theplurality of co-aligned continuous fibers are dispersed substantiallyuniformly throughout the filament subunit.

Aspect 52. The method of any one of aspects 44 to 51, wherein the shapedfilament subunit comprises one or more bends.

Aspect 53 The method of aspect 52, wherein each of the one or more bendsindependently forms an angle within a range from 5° to 179°.

Aspect 54. The method of any one of aspects 44 to 53, wherein the atleast one filament subunit comprises from 1 wt % to 80 wt % of aplurality of co-aligned continuous fibers, wherein wt % is based on thetotal weight of the filament subunit.

Aspect 55. The method of any one of aspects 44 to 54, wherein the atleast one filament subunit comprises from 1 vol % to 80 vol % of aplurality of co-aligned continuous fibers, wherein vol % is based on thetotal volume of the filament subunit.

Aspect 56. A fiber-reinforced composite part fabricated according to themethod of any one of aspects 44 to 55.

Aspect 57. A method of fabricating one or more shaped filament subunits,comprising: securing a section of each of one or more filaments; andshaping the one or more filament sections to provide one or more shapedfilament subunits.

Aspect 58. The method of aspect 57, wherein shaping comprises applyingtension to the one or more filament sections.

Aspect 59. The method of any one of aspects 57 to 58, furthercomprising, before shaping, heating at least a portion of the one ormore filament sections.

Aspect 60. The method of aspect 59, further comprising, after shapingthe one or more filament sections, cooling the heated portion of the oneor more shaped filament sections.

Aspect 61. The method of any one of aspects 57 to 60, wherein, shapingcomprises using dies, rollers, or a combination thereof to shape theheated portion of the one or more filament sections; and coolingcomprises progressively cooling.

Aspect 62. The method of any one of aspects 57 to 61, wherein heating aportion of the one or more filament sections comprises heating theportion of the one or more filament sections simultaneously whileadvancing the one or more filaments.

Aspect 63. The method of any one of aspects 57 to 62, wherein shapingcomprises bending the one or more filament sections.

Aspect 64. The method of any one of aspects 57 to 63, furthercomprising, after shaping the one or more filament sections, separatingthe one or more shaped filament sections from the one or more respectivefilaments.

Aspect 65. The method of any one of aspects 57 to 64, wherein each ofthe one or more filaments independently comprises: a first compositionand a plurality of co-aligned continuous fiber; a second composition anda plurality of non-aligned fiber; or a third composition withoutcontinuous fibers and without non-aligned fibers, wherein each of thefirst composition, the second composition, and the third composition isindependently the same or different than each of the other compositions.

Aspect 66. The method of any one of aspects 57 to 65, wherein shapingcomprises applying the one or more filament sections to a surface.

Aspect 67. The method of any one of aspects 57 to 66, wherein shapingcomprises depositing the one or more filament sections into a cavity.

Aspect 68. The method of any one of aspects 57 to 67, furthercomprising, after shaping, partially curing the one or more shapedfilament sections.

Aspect 69. The method of any one of aspects 57 to 68, furthercomprising, before securing, combining two or more filaments into acombined filament.

Aspect 70. The method of any one of aspects 57 to 69, wherein shapingcomprises embedding a part in the one or more filament sections.

Aspect 71. The method of aspect 70, wherein the part comprises a pin, aninsert, a standoff, an anchor, a shaft, a tube, a connector, a fabric, aunidirectional prepreg, a bidirectional prepreg, or a combination of anyof the foregoing.

Aspect 72. A shaped filament subunit fabricated according to the methodof any one of aspects 57 to 72.

Aspect 73. A filament subunit fabrication apparatus, comprising: afilament feeder configured to advance filament; securing deviceconfigured to secure and to manipulate a section of the advancingfilament; a heating element configured to heat a portion of the securedfilament section; and a shaping element configured to shape and to coolthe heated portion of the filament section.

Aspect 74. The apparatus of aspect 73, wherein, the shaping elementcomprises dies, rollers, or a combination thereof configured to shapethe heated filament section; and the shaping element is configured toprogressively cool the heated portion of the filament section.

Aspect 75. The apparatus of any one of aspects 73 to 74, wherein thesecuring device is configured to hold the advancing filament section intension and to move the heated filament section against the coolingelement.

Aspect 76. The apparatus of any one of aspects 73 to 75, whereinconfigured to shape the heated portion comprises configured to bend theheated portion.

Aspect 77. The apparatus of any one of aspects 73 to 75, wherein, thefilament comprises a co-aligned continuous fiber filament.

Aspect 78. A method of fabricating a part, comprising: securing one ormore filaments to a first anchor; and extending the one or morefilaments in a direction away from the first anchor to provide the part.

Aspect 79. The method of aspect 78, further comprising, during theextension of the one or more filaments, securing the one or morefilaments to one or more second anchors; and further extending the oneor more filaments in a direction away from the one or more secondanchors.

Aspect 80. The method of any one of aspects 78 to 79, wherein extendingcomprises joining filament intersections.

Aspect 81. The method of any one of aspects 78 to 80, wherein fusingfilament intersections comprises applying heat and pressure to thefilament intersections.

Aspect 82. The method of any one of aspects 78 to 81, wherein fusingfilament intersections comprises depositing a composition to thefilament intersections, wherein the composition comprises chopped fiber,milled fiber, or a combination thereof.

Aspect 83. A fiber-reinforced composite part fabricated according to themethod of any one of claims 78 to 82.

Finally, it should be noted that there are alternative ways ofimplementing the embodiments disclosed herein. Accordingly, the presentembodiments are to be considered as illustrative and not restrictive.Furthermore, the claims are not to be limited to the details givenherein, and are entitled to their full scope and equivalents thereof.

1. A fiber-reinforced composite part, comprising one or more sections,wherein at least one section of the one or more sections comprises twoor more fiber bundles, wherein each of the two or more fiber bundlesindependently comprises from 5 to 80,000 continuous fibers impregnatedwith a composition.
 2. The fiber-reinforced composite part of claim 1,wherein each composition independently comprises a matrix material,wherein the matrix material comprises a thermoplastic, a thermoset, or aceramic.
 3. The fiber-reinforced composite part of claim 1, wherein theat least one section comprises: a first fiber bundle comprisingcontinuous fiber having a first configuration; and a second fiber bundlecomprising continuous fiber having a second configuration; wherein thefirst configuration is different than the second configuration.
 4. Thefiber-reinforced composite part of claim 1, wherein the at least onesection comprises: a first fiber bundle comprising a first composition;and a second fiber bundle comprising a second composition, wherein thefirst composition is different than the second composition.
 5. Thefiber-reinforced composite part of claim 1, comprising: a first sectioncomprising a first fiber bundle, wherein the first fiber bundle has afirst configuration; and a second section comprising a second fiberbundle, wherein the second fiber bundle has a second configuration;wherein the first configuration is different than the secondconfiguration. 6-7. (canceled)
 8. The fiber-reinforced composite part ofclaim 1, wherein, the at least one section further comprises one or morenon-fiber portions; and each of the one or more non-fiber portionscomprises a composition without a fiber bundle and without non-alignedfiber.
 9. The fiber-reinforced composite part of claim 1, wherein, theat least one section comprises one or more non-aligned fiber portions;and each of the one or more non-aligned fiber portions comprises acomposition comprising a plurality of non-aligned fibers.
 10. Thefiber-reinforced composite part of claim 1, wherein the at least onesection further comprises a plurality of non-aligned fibers.
 11. Thefiber-reinforced composite part of claim 1, wherein the at least onesection further comprises: one or more non-aligned fiber portionscomprising non-aligned fiber within a composition; one or more non-fiberportions comprising a composition without a fiber bundle and withoutnon-aligned fiber; or both one or more non-aligned fiber portions andone or more non-fiber portions. 12-17. (canceled)
 18. A fiber-reinforcedcomposite part comprising one or more sections, wherein the part isfabricated by: placing two or more filaments into a section of a moldcavity to provide a layup, wherein each of the two or more filamentsindependently comprises a fiber bundle comprising from 5 to 80,000continuous fibers impregnated with a composition; and compressionmolding the layup to provide the fiber-reinforced composite part. 19-31.(canceled)
 32. The fiber-reinforced composite part of claim 1, whereinthe at least one section comprises from 5 vol % to 70 vol % continuousfiber, wherein vol % is based on the total volume of the at least onesection. 33-43. (canceled)
 44. The fiber-reinforced composite part ofclaim 1, wherein, in a cross-section of the at least one section of thepart orthogonal to a length of the two or more fiber bundles, thecontinuous fiber is distributed as bundles of fiber.
 45. Thefiber-reinforced composite part of claim 1, wherein each of the two ormore fiber bundles independently has a cross-sectional dimension inwhich the width dimension is similar to the height dimension
 46. Thefiber-reinforced composite part of claim 1, wherein each of the two ormore fiber bundles independently has a diameter from 0.5 mm to 3 mm. 47.The fiber-reinforced composite part of claim 1, wherein each of the twoor more fiber bundles independently has a cross-sectional dimension lessthan 1 cm.
 48. The fiber-reinforced composite part of claim 1, whereinthe continuous fibers are distributed homogeneously throughout the atleast one section.
 49. The fiber-reinforced composite part of claim 1,wherein the continuous fibers are distributed uniformly throughout theat least one section.
 50. The fiber-reinforced composite part of claim1, wherein the continuous fibers are distributed non-uniformlythroughout the at least one section.
 51. The fiber-reinforced compositepart of claim 1, wherein the continuous fibers are distributed uniformlythroughout the fiber bundle.
 52. The fiber-reinforced composite part ofclaim 1, wherein the continuous fibers are distributed non-uniformlythroughout the fiber bundle.
 53. The fiber-reinforced composite part ofclaim 1, wherein each of the two or more fiber bundles independentlycomprises from 1,000 to 80,000 fibers.
 54. The fiber-reinforcedcomposite part of claim 1, wherein each of the two or more fiber bundlesindependently has a diameter from 0.25 mm to 10 cm.
 55. Thefiber-reinforced composite part of claim 1, wherein each of the two ormore fiber bundles independently has a diameter from 0.5 mm to 3 mm. 56.The fiber-reinforced composite part of claim 1, wherein the fiber bundlehas a round, oval, square, rectangular, or triangular cross-sectionalprofile.
 57. The fiber-reinforced composite part of claim 1, whereineach of the continuous fibers independently has a diameter from 3 μm to20 μm.
 58. The fiber-reinforced composite part of claim 1, wherein eachof the continuous fibers independently has a diameter from 5 μm to 50μm.
 59. The fiber-reinforced composite part of claim 1, wherein the partcomprises two or more shaped filament subunits, wherein each of the twoor more shaped filament subunits comprises a fiber bundle having atleast one bend.